Amcon epoxy Kev Coat - is a two - component, non - solvent and non - hazmat epoxy product, the Resin reinforced with Kevlar fibers and the Curing Agent contains Cycloaliphatic Amin. Whith these reinforcements it has extremely high tensile strength, flexural strength and also improves impact resistance and cohesive strength to create Chip resistance. It is also known for the improved 'Weatherability', water / moisture tolerance,, resistance to blushing and water spotting and better chemical resistance. |
|
|
| |
The unique sealer is designed to dispalce water from wet surfaces and is ideal for underwater application and installations. It can be used above ground and underground repairs. AmCon epoxy Paste is non-corrosive and bonds to a wide range of material such as Metal, Steel, fiberglass, Concrete, Wood and many Plastics.
Surface Preparation
Before applying, the surface must be clean. If possible Sandblasted, and if sandblasting is not possible then through grinding needs to be done to clean the surface. After sandblasting / grinding use cleaner to degrease the surface.
Mixing Ratio
2 part Base : 1 part Cure - Mix until even color is obtained
Applying
it can be applied using the spatula suplied with kit.
Pot Life
Approx. 90 min at 24 °C
Curing Time
Non-Hazmat curing agents generally have a gentler exotherm and slower uniform curing (dosen get super hot, mels containers and urn hard in the blink of an eye). It has a 1 or 2 day 'rubbery' stage and after 48 hrs becomes 'rock hard'.
Machinability
After curing, it can be machined. drilled, etc.
|
|
| |
|
|
| |
| Physical Properties |
|
| Compressive Strength |
10,000 psi |
| Tensile Strength |
4,800 psi |
| CS-17 Wheel, 1Kg Load |
0.10 gm loss |
| Water Absorbtion (2 hour boil) |
0.10% |
| Flexural Strength |
6,600 psi |
| Shore D Hardness |
91 |
| Heat Distortion Temperature |
124 °F |
| Bond Strength To Concrete |
100 % concrete failure |
| Film Thickness |
10-35mils (average:100sq.ft.gallon @ 16mils) |
|
|
| |
|
|
| |
|
|
| |
|
|
|